Interactions of persistent slip bands with a grain boundary on the common primary slip plane in a copper bicrystal

In this letter, the dislocation patterns on the common primary slip plane in a fatigued \1-34]-\182-7] copper bicrystal with a Sigma=19b grain boundary (GB) have been investigated using the electron channelling contrast technique in a scanning electron microscope. The results show that the two-phase dislocation structure, such as veins and persistent slip band (PSB) walls, embedded within veins, can be clearly seen on the common primary slip plane. In particular, the interactions of PSBs with the GB are clearly revealed. It is found that there are three kinds of interaction mode between the GB and the dislocations during cyclic deformation, and those are discussed. It is suggested that the dislocations carried by PSBs cannot transfer through the GB continuously even though the bicrystal has a common primary slip plane and its surface slip bands are continuous across the GB.