Crystallographic texture formation during recrystallization of cold-rolled Fe-3%Si single crystal under high DC magnetic fields |
| |
| Authors: | I V Gervasyeva E Beaugnon V V Gubernatorov T S Sycheva |
| |
| Institution: | 1. Institute of Metal Physics, Ural Branch of the Russian Academy of Sciences, Ekaterinburg, Russia;2. National Laboratory of High Magnetic Field, University of Grenoble Alpes, CNRS-LNCMI, Grenoble, France |
| |
| Abstract: | In a flat single crystal of Fe–3%Si alloy with (1 1 0)0 0 1] orientation, regions with (0 0 1)1.–1.0] orientation (deformation twins) were created by rolling at a low temperature. After cold rolling at 80% at an angle of 45º to the 0 0 1] direction, a (1 1 2) 1.–1.0] deformation texture was formed. In the recrystallization process during annealing of such a sample, a polycrystalline structure having a nearly cubic texture (0 0 1) 1–1.0] is formed. It is demonstrated that annealing under a high DC magnetic field enhances the cubic texture sharpness as compared to annealing carried out under similar conditions without a magnetic field. |
| |
| Keywords: | Texture structure deformation twinning recrystallization |
|
|