Mohsen Seifi Peyman Samimi Iman Ghamarian Peter C. Collins John J. Lewandowski 《Philosophical Magazine Letters》2015,95(11):526-533
Fatigue crack growth experiments were conducted in humid air (RH~45%) at 25 °C on 29-mm-thick plate samples of an aluminium–magnesium (Al–Mg) 5083-H131 alloy in the long transverse (LT) direction. Samples were tested in both the as-received condition and after sensitization at 175 °C for 100 h. Delamination along some grain boundaries was observed in the short transverse plane after fatigue testing of the sensitized material, depending upon the level of ΔK and Kmax. Orientation microscopy using electron backscattering diffraction and chemical analyses using transmission electron microscopy and energy dispersive spectroscopy of grain boundaries revealed that Mg segregation and the orientation of grains had key roles in the observed grain boundary delamination of the sensitized material. 相似文献